In this work, iron ore tailing (IOT) was used for the production of two different materials: sodium silicate and geopolymers. Initially, reactions of IOT with NaOH were carried out by hydrothermal reaction in autoclave at 200 °C (1:1.5 and 1:2.5 SiO2:NaOH molar ratio) and reaction times of 4 and 8 h. X-ray fluorescence by dispersive energy (XRF), X-ray diffraction (XRD), Mössbauer spectroscopy, scanning electron microscopy (SEM-EDS) and titrations showed that IOT:NaOH ratios of 1:2.5 and reaction time 8 h completely dissolved the quartz from the IOT, obtaining a solid fraction consisting mainly of hematite and an aqueous phase of sodium silicate, which showed contents of ca. 23% SiO2 and 19% Na2O. This sodium silicate obtained was then combined with IOT (25 and 50 wt.%) to produce geopolimeric material with excellent physico-chemical properties, fast curing time and very good compressive strength results, which ranged from 41 to 58 MPa and many potential applications.

In this work, we describe a sustainable alternative to recover iron from two iron ore tailings (IOT) using hydrogen reduction at relatively low temperatures followed by magnetic separation. X-ray powder diffraction (XRD), inductively coupled plasma (ICP), atomic absorption (AA), Mössbauer, scanning electron microscopy (SEM/EDS), Raman and thermogravimetry (TG) analyses indicated that the Fe oxide present in the IOTs (sandy tailing (ST) and mud tailings (MT)), can be reduced with H2 at 500 ºC to produce α-Fe. Upon magnetic separation the mud tailing produced a 77 wt.% magnetic fraction increasing the Fe content from 19.2 to ca. 56 wt.% of Fe. On the other hand, the sandy tailing resulted in a 15 wt.% magnetic fraction increasing the Fe content from 19.2 to 70 wt.%. These results indicate that up to 86% of iron can be recovered from the IOT wastes already in the metallic form which can be very interesting for the steel industry.

Considering the bicentenary of Brazil’s Independence in 2022 and that this year was proclaimed by UNESCO as the International Year of Basic Sciences for Sustainable Development, in mid-2021 the Brazilian Chemical Society (SBQ) launched the “Post 2022 Chemistry Movement - Sustainability and Sovereignty”, with the main goal of promoting different activities so that chemistry contributes for the sustainable development and sovereignty of Brazil in the coming years. One of these activities is the proposal of an action plan, with goals to be achieved by 2030 and 2050. This article describes in detail how this action plan was formulated by a working group, with the help of an advisory council and interviews of 18 professionals from universities, the government, industries, the third sector and other organizations. Mimicking the Agenda 2030 SDGs, the resulting action plan is based on two broad Chemistry Sustainable Development Goals: promoting sustainability through chemistry in basic education, and promoting sustainability in the industry and university through science, technology, innovation, and education (STI&E) in chemistry. After the definition of three driving technological challenges in STI&E, they shall be successively implemented through different actions starting in 2023 yet.

Currently, approximately 1.4 billion tons per year of iron ore tailing wastes (IOT) are generated, mainly in Australia, Brazil, and China. This work describes the characterization and application of two typical IOT, i.e., fine and coarse wastes. The physicochemical characterization of these IOT by different techniques such as XRF (X-ray fluorescence), XRD (X-ray diffraction), Mössbauer spectroscopy, and granulometry, indicates for the fine tailing a composition of Fe2O3/FeOOH (10-55%), SiO2 (18-65%) and Al2O3 (up to 15%) with particles of 6-40 µm, whereas the coarse tailing presents 40-150 µm particles with the composition of 8-48% Fe2O3/FeOOH, 30-90% SiO2 and Al2O3 (up to 20%). The main IOT applications discussed in this review are related to civil construction (aggregates for concrete, mortar, Portland cement additives), ceramic industry, geopolymer, synthesis of new materials such as zeolites, mesoporous silica, carbon nanotubes, adsorbents, catalysts for different reactions, in batteries and in fuel cells. It was also carried out an analysis of patents related to IOT applications and the main technological and market barriers that hinder the industrial and commercial uses of these wastes.

In this work, bio-oil (an organic matrix rich in oxygen functionalities) was used to efficiently dissolve and disperse Fe3+ which upon thermal treatment produced a carbon containing dispersed and encapsulated Fe oxide magnetic nanoparticles. These materials were prepared by dissolution of 8, 16 and 24 wt.% Fe3+ salt in bio-oil followed by treatment at 400, 450, 500 or 600 ºC in N2 atmosphere. X-ray diffraction (XRD), scanning (SEM) and transmission electron microscopies (TEM), elemental analysis, thermogravimetric-mass spectrometry (TG-MS), potentiometric titration, Raman and Mössbauer spectroscopies showed that Fe3+ species in bio-oil is reduced to produce magnetic nanoparticles phases: magnetite Fe3O4 and maghemite γ-Fe2O3. At low temperatures, the iron phases were less protected, and the carbon matrix was more reactive, while in temperatures above 500 ºC, the iron phases were more stable, however, the carbon matrix was less reactive. Reaction of these magnetic carbon materials with concentrated H2SO4 produced surface sulfonic acidic sites (ca. 1 mmol g-1), especially for the materials obtained at 400 and 450 ºC. The materials were used as catalysts on esterification reaction of oleic acid with methanol at 100 ºC and conversions of 90% were reached, however, after 2 consecutive uses, the conversion decreased to 30%, being required more studies to improve the material stability.

In this work, a potassium magnesium silicate mineral based on phase K2MgSiO4 was prepared from serpentinite rock and studied as a potential K and Mg slow-release fertilizer. The material was prepared by impregnation of serpentinite/KOH and calcination at 700 °C to produce K2MgSiO4 phase, olivine and forsterite. The release patterns of K and Mg in the stirred-flow trial and leaching through the soil columns showed that K2MgSiO4-based materials released K on lower rates than KCl and MgSO4.7H2O, however, there was no evidence of Mg release. The extraction with 1 mol L-1 NH4OAc showed a considerable content of Mg and K for K2MgSiO4-based materials, due to exchange of NH4+ and Mg2+. X-ray diffraction (XRD) analysis of materials impregnated with K and calcined showed peaks relative to K2MgSiO4. After leaching, the peaks intensity diminished, supporting that part of K leached. Therefore, the samples showed great potential as slow-release K-fertilizers when compared with KCl source.

Porous carbon materials were prepared at low temperatures via thermal decomposition of iron, nickel and cobalt N, N -diethyldithiocarbamates (DDT). X-ray diffraction data showed two peaks at 2θ (25.5º and 43.5º) that indicate the presence of graphite-like structures. Raman spectra displayed D and G bands in the range from 1312 to 1321 cm-1 and 1587 to 1593 cm-1, respectively, which were fitted with 4 components. All spectra showed two low intensity D* (1190 cm-1) and D’’ (1500 cm-1) bands, assigned to sp2–sp3 bonds in disordered carbonaceous materials and amorphous carbon, respectively. Transmission electron microscopy images showed agglomerates of spherical particles formed by graphitic segments. The results showed that the carbon material obtained from iron N, N -diethyldithiocarbamate, Fe(DDT)3, is structurally better organized than the others and the pore size distribution curves confirmed that this material presents high degree of mesoporosity. Voltammetric curves obtained using KOH and H2SO4 electrolytes showed hysteresis behavior typical of capacitors charge/discharge process. The carbon material prepared from Fe(DDT)3 displayed the highest specific capacitance in acidic media, 59 F g-1, which was associated to its high degree of mesoporosity.

Solid state reaction of serpentinite Mg3Si2O5(OH)4 with NaOH was investigated to produce new NaMgSi oxide phases with basic properties for application in catalysis. X-ray powder diffraction (XRD) showed that NaOH impregnated on serpentinite, specially 20% sodium and treated at 700 ºC (20Na700), led to the formation of a new crystalline phase Na2Mg2Si2O7. This solid state reaction is discussed in terms of a first step involving Na+ diffusion and intercalation in the interlayer space of the serpentinite structure followed by a dihydroxylation and formation of the NaMgSi oxides. Temperature programmed reaction and desorption experiments with 20Na700 combined with XRD suggested a strong basicity with high CO2 uptake likely due to diffusion and interaction with the basic sites in the material structure. These materials were tested as catalysts for the transesterification of soybean oil with methanol. The obtained results are discussed in terms of a basic site Si-O-Na+ present in the in the Na2Mg2Si2O7 structure.

Ferro é um elemento versátil que forma várias fases com diferentes estados de oxidação e estruturas, tais como Feº, FeO, Fe3O4, γ-Fe2O3, α-Fe2O3 e FeOOH. Todas estas fases têm propriedades físico-químicas únicas que podem ser usadas para diferentes aplicações. Neste trabalho, descreve-se o uso de diferentes compostos de ferro, sintéticos e também naturais ou de rejeitos, em aplicações ambientais e tecnológicas. Duas áreas principais de pesquisa são descritas. A primeira é relacionada às estratégias para aumentar a reatividade de fases de ferro pela formação de compósitos Feº/Fe óxido e pela introdução de novos metais na estrutura de óxidos de ferro para promover novas reações superficiais. A segunda área de pesquisa é o uso das propriedades magnéticas de algumas fases de ferro para produzir materiais magnéticos versáteis com aplicações focadas em adsorção, catálise e emulsões.

Iron is a versatile element forming several phases with different oxidation states and structures, such as Feº, FeO, Fe3O4, γ-Fe2O3, α-Fe2O3 and FeOOH. All these phases have unique physicochemical properties which can be used for different applications. In this work, it is described the use of different iron compounds, synthetic and also from natural and waste sources, in environmental and technological applications. Two main research areas are described. The first one is related to strategies to increase the reactivity of Fe phases, mainly by the formation of Feº/iron oxide composites and by the introduction of new metals in the iron oxide structure to promote new surface reactions. The second area is the use of the magnetic properties of some iron phases to produce versatile magnetic materials with focus in adsorption, catalysis and emulsions.